Investigation on magnetic properties of mechanically alloyed τ-MnAlC with Fe addition - Le Mans Université Accéder directement au contenu
Article Dans Une Revue Journal of Magnetism and Magnetic Materials Année : 2021

Investigation on magnetic properties of mechanically alloyed τ-MnAlC with Fe addition

Résumé

The influence of Fe addition on thermal stability, crystallography, and magnetic properties of τ-Mn51Al47C2 was investigated. Alloys with composition Mn51-xFexAl47C2 (x = 0, 0.5, 1, 2, and 4) were synthesized by mechanical alloying method. High purity of τ-Mn(Fe)AlC up to 98% could be obtained after 10 h of milling, then annealed at 1050 °C for 1 h, and followed by an aging process at appropriate temperatures from 515 to 540 °C for 50 min. It was found that the thermal stability of both ε and τ phases was enhanced by the addition of Fe up to 4 at.% into MnAlC alloy through a shifting of ε-to-τ transformation temperature to high temperature region and a reduction in c/a ratio of Fe doped τ-MnAlC compared to iron free τ-MnAlC. While the magnetization and Curie temperature of Fe doped τ-MnAlC showed a reduction compared to iron free τ-Mn51Al47C2, coercivity seems not to be significantly affected. Ab initio calculation showed a lower magnetic moment of Fe (μFe = 1.77 μB) compared to Mn (μMn_average = 2.36 μB) in τ-Mn(Fe)AlC when Fe substituted Mn position at 1a site.
Fichier principal
Vignette du fichier
preprint_Nguyen Van Tang_revised.pdf (2.26 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-03454133 , version 1 (29-11-2021)

Identifiants

Citer

Van Tang Nguyen, Frédéric Mazaleyrat, Florent Calvayrac, Quang Minh Ngo, Nirina Randrianantoandro. Investigation on magnetic properties of mechanically alloyed τ-MnAlC with Fe addition. Journal of Magnetism and Magnetic Materials, 2021, pp.168892. ⟨10.1016/j.jmmm.2021.168892⟩. ⟨hal-03454133⟩