X-ray scattering and EXAFS studies of Pt1−xVx alloys

Alain Gibaud
Gwenaël Corbel
V. Briois
  • Fonction : Auteur
D. Thiaudiere
  • Fonction : Auteur
T. Ntsoane
  • Fonction : Auteur

Résumé

Alloys of the Pt–V system between 0 and 50 at.% V have been investigated by X-ray scattering and extended X-ray absorption fine structure (EXAFS). The variation of lattice parameter with the nominal chemical composition was measured and compared to previously reported values. The solid solution was observed in alloys containing up to 20 at.% V. In the alloy with higher vanadium concentration, 50 at.% V, we found that the alloy is not homogeneous and exhibits a segregation of Pt and PtV phases in addition to VO2(M) phase. These experiments are complemented by EXAFS measurements made at the K edge of V which clearly show the sensitivity of this technique to V content. Determination of the local environment of V and Pt is made via a basic model taking in account the first neighbours only. A discussion is presented about the comparison between X-ray and EXAFS results obtained from the same samples.
Fichier non déposé

Dates et versions

hal-02138603 , version 1 (23-05-2019)

Identifiants

Citer

Alain Gibaud, M. Topić, Gwenaël Corbel, V. Briois, D. Thiaudiere, et al.. X-ray scattering and EXAFS studies of Pt1−xVx alloys. Journal of Alloys and Compounds, 2013, 562, pp.95-98. ⟨10.1016/j.jallcom.2013.01.059⟩. ⟨hal-02138603⟩
23 Consultations
0 Téléchargements

Altmetric

Partager

Gmail Facebook Twitter LinkedIn More