Synthesis of La2Mo2O9 powders with nanodomains using polyol procedure - Le Mans Université Accéder directement au contenu
Article Dans Une Revue Ceramics International Année : 2013

Synthesis of La2Mo2O9 powders with nanodomains using polyol procedure

Résumé

Powders of oxide-ion conductor La2Mo2O9 presenting nanodomains were synthesized by using polyol processes. The influence of different process parameters on the structure and particles morphology was determined. By the classical polyol process, whatever the polyol solvent used (ethylene glycol, diethylene glycol, 1,2-propanediol and tetraethylene glycol) platelet particles with dimensions of few hundred nanometers long and around twenty nanometers thick were observed, as agglomerates of small sub-particles. Only with diethylene glycol, pure La2Mo2O9 was obtained, whereas with microwave assistance, ethylene glycol also leads to pure product. For both ethylene and diethylene glycol solvent, the microwave assisted process resulted in either agglomerates or desert roses conglomerates after heat treatments at 500 degrees C for 5 min or 2 h. Specific surface areas, ranging between 23 and 36 m(2) g(-1), have been measured for pure La2Mo2O9 powders.
Fichier principal
Vignette du fichier
Accepted Manuscript_13-Sellemi_La2Mo2O9 nanodomains by polyol process_CERI39-8853.pdf (4.13 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

hal-02173914 , version 1 (04-07-2019)

Identifiants

Citer

Houssem Sellemi, Sandrine Coste, Amor Ben Ali, Richard Retoux, Leila Samia Smiri, et al.. Synthesis of La2Mo2O9 powders with nanodomains using polyol procedure. Ceramics International, 2013, 39 (8), pp.8853-8859. ⟨10.1016/j.ceramint.2013.04.076⟩. ⟨hal-02173914⟩
107 Consultations
90 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More