Compatibility evaluation between La2Mo2O9 fast oxide-ion conductor and Ni-based materials

(1) , (1)
1
Gwenaël Corbel
Philippe Lacorre

Résumé

The chemical reactivity of La2NiO4+delta and nickel metal or nickel oxide with fast oxide-ion conductor La2Mo2O9 is investigated in the annealing temperature range between 600 and 1000°C, using room temperature X-ray powder diffraction. Within the La2NiO4+delta/ La2Mo2O9 system, subsequent reaction is evidenced at relatively low annealing temperature (600°C), with formation of La2MoO6 and NiO. The reaction is complete at 1000 1C. At reverse, no reaction occurs between Ni or NiO and La2Mo2O9 up to 1000°C. Together with a previous work [G. Corbel, S. Mestiri, P. Lacorre, Solid State Sci. 7 (2005) 1216], the current study shows that Ni-CGO cermets might be chemically and mechanically compatible anode materials to work with LAMOX electrolytes in solid oxide fuel cells.

Dates et versions

hal-02134996 , version 1 (20-05-2019)

Identifiants

Citer

Gwenaël Corbel, Philippe Lacorre. Compatibility evaluation between La2Mo2O9 fast oxide-ion conductor and Ni-based materials. Journal of Solid State Chemistry, 2006, 179 (5), pp.1339-1344. ⟨10.1016/j.jssc.2006.01.051⟩. ⟨hal-02134996⟩

Collections

UNIV-LEMANS
19 Consultations
0 Téléchargements

Altmetric

Partager

Gmail Facebook Twitter LinkedIn More