Quasi-static and fatigue properties of a balsa cored sandwich structure with thermoplastic skins reinforced by flax fibres - Archive ouverte HAL Accéder directement au contenu
Article Dans Une Revue Journal of Sandwich Structures and Materials Année : 2018

Quasi-static and fatigue properties of a balsa cored sandwich structure with thermoplastic skins reinforced by flax fibres

(1) , (1) , (2) , (3)
1
2
3

Résumé

This paper presents the results of several experimental analyses performed on a biobased sandwich structure. The material studied is made up of thermoplastic skins reinforced by flax fibres and applied to a balsa core. It is produced by a single-step liquid resin infusion process. First, the skin–core interfacial properties were measured and compared with those of the existing materials. Then, several quasi-static and dynamic analyses were performed to study the flexural behaviour of sandwich beams. The elastic and ultimate properties of the skins and core were deduced from these flexural tests. In addition, a failure mode map was developed based on the existing theories to explain the failure modes observed under different boundary conditions. The influence of the statistical spread of the core’s mechanical properties on the failure of sandwich beams was considered. Moreover, fatigue analyses were conducted to determine the fatigue resistance of this bio-based structure. Its behaviour was compared with that of the previously tested non-bio-based sandwich beams.
Fichier principal
Vignette du fichier
LAMPA_JSSN_2018_GUILLAUMAT.pdf (982.68 Ko) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

hal-02406518 , version 1 (12-12-2019)

Identifiants

  • HAL Id : hal-02406518 , version 1

Citer

Arthur Monti, Abderrahim El Mahi, Zouhaier Jendli, Laurent Guillaumat. Quasi-static and fatigue properties of a balsa cored sandwich structure with thermoplastic skins reinforced by flax fibres. Journal of Sandwich Structures and Materials, 2018, 21 (7), pp.2358-2381. ⟨hal-02406518⟩
72 Consultations
166 Téléchargements

Partager

Gmail Facebook Twitter LinkedIn More